Title: Ultrasound assisted dispersal of a copper nanopowder for electroless copper activation
Authors: Graves, John E.
Sugden, Mark
Litchfield, Robert E.
Hutt, David A.
Mason, Timothy J.
Cobley, Andrew J.
Keywords: Ultrasound
Copper nanoparticles
Catalytic ink
Electroless copper
Issue Date: 2016
Publisher: © Elsevier
Citation: GRAVES, J.E. ... et al, 2016. Ultrasound assisted dispersal of a copper nanopowder for electroless copper activation. Ultrasonics Sonochemistry, 29, pp. 428 - 438.
Abstract: This paper describes the ultrasound assisted dispersal of a low wt./vol.% copper nanopowder mixture and determines the optimum conditions for de-agglomeration. A commercially available powder was added to propan-2-ol and dispersed using a magnetic stirrer, a high frequency 850 kHz ultrasonic cell, a standard 40 kHz bath and a 20 kHz ultrasonic probe. The particle size of the powder was characterized using dynamic light scattering (DLS). Z-Average diameters (mean cluster size based on the intensity of scattered light) and intensity, volume and number size distributions were monitored as a function of time and energy input. Low frequency ultrasound was found to be more effective than high frequency ultrasound at de-agglomerating the powder and dispersion with a 20 kHz ultrasonic probe was found to be very effective at breaking apart large agglomerates containing weakly bound clusters of nanoparticles. In general, the breakage of nanoclusters was found to be a factor of ultrasonic intensity, the higher the intensity the greater the de-agglomeration and typically micron sized clusters were reduced to sub 100 nm particles in less than 30 min using optimum conditions. However, there came a point at which the forces generated by ultrasonic cavitation were either insufficient to overcome the cohesive bonds between smaller aggregates or at very high intensities decoupling between the tip and solution occurred. Absorption spectroscopy indicated a copper core structure with a thin oxide shell and the catalytic performance of this dispersion was demonstrated by drop coating onto substrates and subsequent electroless copper metallization. This relatively inexpensive catalytic suspension has the potential to replace precious metal based colloids used in electronics manufacturing.
Description: This paper was accepted for publication in the journal Ultrasonics Sonochemistry and the definitive published version is available at http://dx.doi.org/10.1016/j.ultsonch.2015.10.016
Sponsor: The authors would like to thank the EPSRC for funding this research through the Innovative Electronics Manufacturing Research Centre (IeMRC), Grant Number EP/H03014X/1. In addition, the authors are grateful to the industrial collaborators, Chestech Ltd, Printed Electronics Ltd and Graphic Plc for technical support and provision of materials.
Version: Accepted for publication
DOI: 10.1016/j.ultsonch.2015.10.016
URI: https://dspace.lboro.ac.uk/2134/20712
Publisher Link: http://dx.doi.org/10.1016/j.ultsonch.2015.10.016
ISSN: 1350-4177
Appears in Collections:Published Articles (Mechanical, Electrical and Manufacturing Engineering)

Files associated with this item:

File Description SizeFormat
Manuscript Ultrasonic assisted dispersal of Cu Nanopowder For repository.pdfAccepted version1.6 MBAdobe PDFView/Open


SFX Query

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.