Title: Effect of POSS on crystalline transitions and physical properties of polyamide 12
Authors: Wan, Chaoying
Zhao, Feng
Bao, Xujin
Kandasubramanian, Bala
Duggan, Matthew P.
Keywords: Crystalline transition
Physical properties
Issue Date: 2009
Publisher: © Wiley Periodicals
Citation: WAN, C. ... et al., 2009. Effect of POSS on crystalline transitions and physical properties of polyamide 12. Journal of Polymer Science. Part B, Polymer Physics, 47 (2), pp.121-129.
Abstract: Polyamide 12/Trisilanolphenyl-POSS (PA 12/POSS) composites were prepared via melt-compounding. The effect of polyhedral oligomeric silsesquioxane (POSS) on crystalline structure and crystalline transition of PA 12 was investigated by wide-angle X-ray diffraction (WAXD) and real time fourier transform infrared spectroscopy (FTIR). WAXD results indicated that PA 12 crystallized into γ-form as slowly cooling from melt and the presence of POSS did not influence the crystalline structure of PA 12. Both PA 12 and PA 12/POSS composites underwent Brill transitions when they were heated from room temperature to melt point. Real time FTIR patterns showed that an absorption band at 697 cm−1 ascribed to Amide V (α) mode was emerged along with the disappearance of Amide VI (γ) band at 628 cm−1 with the increase of the temperature for PA 12 and PA 12/POSS composites, which suggested that the γ-form crystalline has transformed into α form. The Brill bands were identified and the transformed mechanism was discussed based on the real FTIR results. The addition of POSS enhanced the tensile strength and thermal stability of PA 12.
Description: Closed access.
Sponsor: The authors gratefully acknowledge the financial support of National Natural Science Foundation of China (50803035) and theUKDepartment of Trade and Industry/ Technology Stategy Board.
Version: Published
DOI: 10.1002/polb.21620
URI: https://dspace.lboro.ac.uk/2134/22430
Publisher Link: http://dx.doi.org/10.1002/polb.21620
ISSN: 0887-6266
Appears in Collections:Closed Access (Materials)

Files associated with this item:

File Description SizeFormat
Journal of Polymer Science.pdfPublished version899.03 kBAdobe PDFView/Open


SFX Query

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.