Densification of nanostructured YSZ green compacts
journal contribution
posted on 2007-01-22, 11:37 authored by Vaidhy VaidhyanathanVaidhy Vaidhyanathan, J.G.P. BinnerConventional and microwave sintering experiments have been performed on
nanocrystalline yttria partially stabilised zirconia (Y-PSZ) green compacts produced by die pressing
and slurry casting. Whilst one of the nanopowders used developed spherical inclusions measuring 1
– 4 μm in diameter during sintering, the combination of microwave sintering and the second
nanopowder yielded sintered bodies of >97% of theoretical density and with an avConventional and microwave sintering experiments have been performed on
nanocrystalline yttria partially stabilised zirconia (Y-PSZ) green compacts produced by die pressing
and slurry casting. Whilst one of the nanopowders used developed spherical inclusions measuring 1
– 4 μm in diameter during sintering, the combination of microwave sintering and the second
nanopowder yielded sintered bodies of >97% of theoretical density and with an average grain size
of 140 nm.
History
School
- Aeronautical, Automotive, Chemical and Materials Engineering
Department
- Materials
Pages
2880840 bytesCitation
VAIDHYANATHAN, B. and BINNER, J.G.P., 2004. Densification of nanostructured YSZ green compacts. Key Engineering Materials, 264-268, pp. 2339-2342.Publisher
© Trans TechPublication date
2004Notes
This is Closed Access. This article was published in the journal, Key Engineering Materials [© Trans Tech] and is available at: www.scientific.net.ISSN
1013-9826Language
- en